Polyvinyl Alcohol (PVA) -Wanwei
Paglalarawan
Panimula
Ang Anhui Wanwei High-tech Materials Co., Ltd. ay nagpaproduk ng mga produkto sa serye ng polyvinyl alcohol (PVA) na brand ng "Wanwei" gamit ang unang-klaseng teknolohiya at pamamaraan, isa ay vinyl acetate na ginawa mula sa calcium carbide acetylene method at petroleum ethylene method bilang materyales, ang iba naman ay ethylene na ginawa mula sa biyolohikal na alkohol bilang materyales, methanol bilang solvent, peroxide bilang initador, sa pamamagitan ng polymerization, alcoholysis at iba pang proseso.
Detalye ng produkto
Kimikal na Pangalan: POLYVINYL ALCOHOL (PVA)
Molekular na pormula: -[CH2CH(OH)]n
Mga pisikal na katangian:
Ang anyo ay puting flake, granular o powdery solid (mula sa low alkali alcoholysis process) o puting flocculent solid (mula sa high alkali alcoholysis process). Partikular na timbang: 1.19-1.31 g/cm 3, flake PVA filling specific gravity: 0.42-0.52 g/cm 3, flocculent filling specific gravity: 0.20-0.27 g/cm 3.
Katangian kimikal:
Nakakatunaw sa tubig: Ang mga molekula ng PVA ay madaling natutunaw sa tubig dahil ito ay naglalaman ng maraming bilang ng mga grupo ng hydroxyl. Ang pagtutunaw nito ay tumataas kasabay ng pagtaas ng temperatura ng tubig, lumuluwag lamang sa malamig na tubig (mga produkto na may mababang alcoholysis ay maaaring dahan-dahang matunaw sa tubig na may normal na temperatura), at ganap na natutunaw sa mainit na tubig. Ang kanyang tubig na solusyon ay may magandang kakaukulang film-forming at cohesive properties.
Thermal Stability: Ang produkto ay yumayapos kapag pinainit, hindi gaanong nagbabago sa ilalim ng 40℃, mahabang pag-init sa 160℃ ay unti-unting magdudulot ng pagbabago ng kulay, ang pagkasira ay nangyayari sa taas ng 220℃, na nagreresulta sa pagbuo ng tubig, asukat, aldehydo at butenal.
Resistensya sa Kemikal: Ang produkto ay halos hindi apektado ng mahina asido, mahina basiko o organic solvent, at may mataas na resistensya sa langis.
Estabilidad ng imbakan: Mabuting katatagan ng produkto, matagalang imbakan sa likas na tuyong estado ay hindi bubuo ng amag, hindi mabubulok, at hindi hihila ng kahalumigmigan.
Ang PVA ay isang polimero na may pangalawang grupo ng hydroxyl. Ang pangalawang grupo ng hydroxyl sa pormula ng molekula ng PVA ay may mataas na reaktibidad, at maaaring makagawa ng mga tipikal na kemikal na reaksiyon katulad ng mababang molekular na alkohol, tulad ng esterification, etherification, acetalization, atbp., at maaari ring makireho sa maraming inorganikong kompuwesto at organikong kompuwesto. Hindi nakakalason sa tao at hayop, natural na nabubulok, kilala bilang berdeng produkto.
Bawat produktong talaksan
Item |
Hidrolisis (mol%) |
Ang viscosity (mpa.s) |
Ligtas (%≤) |
Abo (%≤) |
PH (Bilang) |
03-88（L） |
85.0-90.0 |
2.5-3.5 |
≤7.0 |
≤0.7 |
5~7 |
03-97（L） |
95.0-99.0 |
3.0-4.0 |
≤7.0 |
≤0.7 |
5~7 |
04-88(L) |
85.0-90.0 |
3.5-4.5 |
≤7.0 |
≤0.7 |
5~7 |
04-99（L） |
98.0-99.8 |
3.5-4.5 |
≤7.0 |
≤0.7 |
5~7 |
05-88（L） |
85.0-90.0 |
4.5-6.5 |
≤7.0 |
≤0.7 |
5~7 |
05-99（L） |
98.0-99.8 |
4.5-7.0 |
≤7.0 |
≤0.7 |
5~7 |
08-88（L） |
85.0-90.0 |
6.5-8.0 |
≤7.0 |
≤0.7 |
5~7 |
08-99（L） |
98.0-99.8 |
7.0-9.0 |
≤7.0 |
≤0.7 |
5~7 |
10-88（L） |
85.0-90.0 |
8.0-11.0 |
≤7.0 |
≤0.7 |
5~7 |
10-99 (L) |
98.0-99.8 |
8.0-12.0 |
≤7.0 |
≤0.7 |
5~7 |
13-88 (L) |
86.0-90.0 |
11.0-14.0 |
≤7.0 |
≤0.7 |
5~7 |
14-92 (L) |
90.0-94.0 |
13.0-17.0 |
≤7.0 |
≤0.7 |
5~7 |
15-99 (L) |
98.0-99.8 |
13.0-18.0 |
≤7.0 |
≤0.7 |
5~7 |
17-88 (L) |
85.0-90.0 |
20.0-28.0 |
≤7.0 |
≤0.7 |
5~7 |
17-92（L） |
90.0-94.0 |
20.0-28.0 |
≤7.0 |
≤0.7 |
5~7 |
17-98（L） |
97.0-99.0 |
24.0-32.0 |
≤7.0 |
≤0.7 |
5~7 |
17-99 (L) |
99.0-100.0 |
22.0-32.0 |
≤7.0 |
≤0.5 |
5~7 |
20-88（L） |
85.0-90.0 |
28.0-40.0 |
≤7.0 |
≤0.5 |
5~7 |
20-92（L） |
90.0-94.0 |
29.0-40.0 |
≤7.0 |
≤0.7 |
5~7 |
20-99（L） |
99.0-100.0 |
35.0-48.0 |
≤7.0 |
≤0.7 |
5~7 |
24-88（L） |
85.0-90.0 |
43.0-58.0 |
≤7.0 |
≤0.7 |
5~7 |
24-99（L） |
99.0-100.0 |
65.0-85.0 |
≤7.0 |
≤1.0 |
5~7 |
26-99（L） |
99.0-100.0 |
85.0-100.0 |
≤7.0 |
≤0.7 |
5~7 |
17-99 (H) |
99.0-100.0 |
20.0-26.0 |
≤8.0 |
≤2.8 |
7~10 |
19-99（H） |
99.0-100.0 |
26.0-34.0 |
≤8.0 |
≤2.8 |
7~10 |
20-99（H） |
99.0-100.0 |
34.0-42.0 |
≤8.0 |
≤2.8 |
7~10 |
23-99（H） |
99.0-100.0 |
42.0-55.0 |
≤6.5 |
≤2.5 |
7~10 |
22-99（H） |
99.0-100.0 |
42.0-55.0 |
≤8.0 |
≤2.8 |
7~10 |
24-99（H） |
99.0-100.0 |
55.0-65.0 |
≤8.0 |
≤2.8 |
7~10 |
Paggamit ng Produkto
Pandikit
Ang polyvinyl alcohol sa mga pandikit ay naging isang solusyon sa paghabi na multi-scenario sa pamamagitan ng tatlong-in-one na mekanismo ng "polar adhesion-film enhancement-chemical modification". Ang kanyang core value ay nakasalalay sa kaligtasan at pangangalaga sa kapaligiran, malawak na bonding, at madaling pagbabago, at lalo na angkop para sa cellulose substrates.
Coating
Ang Polyvinyl alcohol ay naging isang "performance bridge" sa sistema ng pintura sa pamamagitan ng apat na mekanismo: film-forming reinforcement, interface bonding, construction optimization, at functional modification. Ang kanyang core value ay nakasalalay sa balanse ng rigidity at flexibility (pinapabuti ang crack resistance at pagkapit ng pintura), water-air regulation (nagsasaalang-alang pareho ng waterproof at breathable na kinakailangan), at environmental protection at ekonomiya (hindi nakakalason, biodegradable, at binabawasan ang dami ng emulsyon). Ang pagpili ay dapat isama ang application scenario.
Pagproseso ng Papel
Sa proseso ng papel, ang polyvinyl alcohol ay naging isang multifunctional na additive na nagpapabuti sa kumpletong pagganap ng papel sa pamamagitan ng tatlong-in-one na mekanismo ng "surface film formation-pigment bonding-fiber reinforcement". Ito ay may malaking bentahe sa mga tuntunin ng lakas, printability, water resistance at environmental protection, at lalo na hindi mapapalitan sa high-end na papel at specialty paper.
Warp Yarn Sizing
Ang Polyvinyl alcohol ay ginagamit bilang isang sizing agent upang palakasin ang lakas ng sinulid at lumaban sa pagsusuot, bawasan ang rate ng pagkabigo ng sinulid habang hinahabi, at mapabuti ang kalidad ng tela.
Mga Pakete
20 kg/sakong, 25 kg/sakong.